| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
比重 | 1.36 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 50 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.3 % | Internal | 1/8" bar |
吸水率 | 2.1 % | ASTM D570 | 50% RH |
吸水率 | 6.6 % | ASTM D570 | Saturation |
吸水率 | 2.1 % | ISO 62 | 50% RH |
吸水率 | 6.6 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 115 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 185 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 179 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3.3 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 8 % | ISO 527 | Conditioned,23℃ |
断裂(brk) | 4 % | ISO 527 | Dry,-40℃ |
断裂(brk) | 3.5 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 180 Mpa | ISO 178 | Conditioned,23℃ |
- | 270 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 8280 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 5000 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 8600 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 6200 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 9500 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 11 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 30 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 15 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 80 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 110 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 95 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 107 J/m | ASTM D256 | Dry |
23℃ (73℉) | 134 J/m | ASTM D256 | Dry |
23℃ (73℉) | 20 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 207 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 90 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 95 °C | UL 746B | |
电气Elec,0.75/0.8mm | 130 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 130 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 130 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 130 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 23 E-6/°C | Internal | Dry |
横向(Across Flow) | 65 E-6/°C | Internal | Dry |
- | 10 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-m | ASTM D257 | Conditioned,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | 1.0E+10 Ohm-m | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
介电常数(DK) | |||
1MHz | 6.8 - | IEC 60250 | Conditioned |
1MHz | 3.8 - | IEC 60250 | Dry |
耗散因数(DF) | |||
1MHz | 2200 E-4 | IEC 60250 | Conditioned |
1MHz | 230 E-4 | IEC 60250 | Dry |
PA6应用：工业生产中泛用于制造轴承、圆齿轮、凸轮、伞齿轮、各种滚子、滑轮、泵叶轮、风扇叶片、蜗轮、推进器、螺钉、螺母、垫片、高压密封圈、耐油密封垫片、耐油容器、外壳、软管、电缆护套、剪切机、滑轮套、牛头刨床滑块、电磁分配阀座、冷陈设备、衬垫、轴承保持架、汽车和拖拉机上各种输油管、活塞、绳索、传动皮带，纺织机械工业设备零配件等。
优点：
1). 强度和耐久性，优良的刚性和耐热性的结合
2). 优化部件设计，优异的着色性能，完美的表面外观，能够适用于复杂的结构成型，并帮助设计开发者开发新造型产品
3). 良好的加工性，优异的流动性及热稳定性使材料加工条件更为宽松，使注塑件微型化
4). 极高的热稳定性，能在高达270度的波峰焊锡中不挂锡
5). 广泛的温度和频率范围内恒定的电气性，确保装置设备的使用安全。
PA6在汽车领域中的应用
内外饰部件
汽车用高性能增强尼龙6复合材料具有优异的耐气候性、良好的油漆性能和杰出的表现效果，为了满足在内外饰方面的使用要求，增强尼龙6材料应具备以下要求：
1). 高耐热，长期使用；
2）优异的刚性和韧性的结合；
3). 能够满足强烈的温度和湿度的不断变化而承受巨大的应变；
4). 出色的尺寸稳定性，具有防翘曲的效果；
5). 具有高表面质量，表面光洁。
发动机周边部件
汽车用高性能增强尼龙6复合材料制造发动机周边部件，如进气歧管、发动机罩盖等，可以代替传统金属材料，为了满足在发动机周边部件的使用要求，尼龙6材料应具备以下优点：
1). 优异的强度和韧性，满足结构部件的机械性能；
2). 出色的耐热性，可以在高达130℃温度下连续使用；
3). 长期的耐疲劳性，热老化后性能保持好；
4). 出色的尺寸稳定性，具有防翘曲的效果；
5). 表面效果好，无浮纤；
6). 耐油性好，耐腐蚀性佳。
温馨提示:因产品行情浮动频繁,实时价格详情请来电咨询.不便之处敬请谅解！
您如果对我们的产品感兴趣或者有任何的疑问，您可以直接给我们留言或直接与我们联络，
我们将在收到您的信息后，及时与您联络，我们衷心的希望能与各届朋友合作，携手未来，合作共赢