| POM 7520 日本旭化成 |
| 规格级别： | 高流动等级 | 外观颜色： | --- |
| 用途概述： | 打火机、喷雾器阀门零件、紧固件 | ||
| 备注说明： | 适合于薄壁、长流动距离的注塑 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸湿率 | --- | ASTM D-570 | 0.2 | % |
| 熔体流动速率 | --- | ASTM D-1238 | 30 | gr/10min | |
| 物理性能 | 磨耗率 | --- | ASTM D-1044 | 14 | mg/1000次 |
| 成型收缩率 | --- | 旭化成方法 | 1.6-2.0 | % | |
| 比重 | --- | ASTM D-792 | 1.41 | --- | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 61 | MPa |
| 延伸率 | --- | ASTM D-638 | 50 | % | |
| 抗挠强度 | --- | ASTM D-790 | 90 | MPa | |
| 抗挠系数 | --- | ASTM D-790 | 2630 | MPa | |
| 悬臂梁式缺口冲击强度 | --- | ASTM D-256 | 59 | J/M | |
| 洛氏硬度 | --- | ASTM D-785 | 80 | M scale | |
| 洛氏硬度 | --- | ASTM D-785 | 115 | R scale | |
| 热 性 能 | 线性膨胀系数 | --- | TMA | 10 | ×10-5cm/cm℃ |
| 阻燃性 | --- | UL 94 | HB | --- | |
| 热变形温度 | 1.82MPa | ASTM D-645 | 110 | ℃ | |
| 热变形温度 | 0.45MPa | ASTM D-645 | 158 | ℃ | |