Teflon® PTFE
TE3859/TE3893: General-purpose resin composed of 60% PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 通用树脂组成的60％聚四氟乙烯分散在水中。包含非离子润湿剂和稳定剂。)
TE3864: TE3864 replaces Teflon® PTFE B; aqueous dispersion containg 61%, by total weight, of active ingredients. Special formulation designed for application to woven glass fabric used to make bags for difficult gaseous filtration or product collection systems. Excellent hydrophobisity and chemical resistance(TE3864取代特富龙®聚四氟乙烯乙;水分散体总重的有效成分，containg61％。特殊配方设计中的应用玻璃纤维织物用于弥补困难气体过滤袋或产品的收集系统。优秀hydrophobisity和耐化学性)
TE3875/TE3876: Good gloss, high shear stability and good weldability; improved abrasion resistance, flex-life and color. 60% PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 光泽度好，高剪切稳定性和良好的可焊性，改善耐磨性，弹性，生命和颜色。 60％的聚四氟乙烯分散于水中。包含非离子润湿剂和稳定剂)
TE3885/TE3908: Resin composed of approximately 61% PTFE dispersed in water. Contains a nonionic wetting agent and stabilizer.( 树脂组成的约61％聚四氟乙烯分散在水中。包含非离子润湿剂和稳定剂)
TE3890: Resin composed of nominal 35% PTFE dispersed in water with an anionic wetting agent.( 树脂组成的名义35％聚四氟乙烯分散在水中的阴离子润湿剂)
6C: General-purpose resin. Medium reduction ratio. Excellent color and clarity. Accepts filler exceptionally well.( 通用树脂。中等缩小比例。出色的色彩和清晰度。接受填料出色)
60: Low reduction ratio. High-pressure resin.( 低减速比。高压树脂)
62: Premium resin offers highest thermal stability, stress crack resistance, flex life, and clarity of all grades. Low to medium reduction ratio.( 高级树脂提供了最高的热稳定性，耐应力开裂，弯曲的生活，和所有级别的清晰度。低到中等缩小比例)
601A: High molecular weight. Low reduction ratio. Excellent thermal stability.( 高分子量。低减速比。优良的热稳定性)
602A: Low reduction ratio. Medium molecular weight. Excellent thermal stability.( 低减速比。中等分子量。优良的热稳定性)
610A: Medium to high reduction ratio.( 中到高减速比)
613A: Low reduction ratio.( 低减速比)
CFP6000: High reduction ratio. Low-pressure resin.( 高压缩比。低压树脂)
7A: Finely divided 35-micron particles. 460-g/L bulk density. Up to 5,500 psi in tensile strength. Maximum granular PTFE chemical resistance. Parts fabricated from this resin have excellent physical and electrical properties.( 精细分割35微米的颗粒。 460 g / L的体积密度。高达5500 psi的拉伸强度。最大颗粒聚四氟乙烯的耐化学性。这种树脂制成的零件具有优异的物理和电气性能)
7C: Finely divided "fluffy" 20-micron particles. 250-g/L bulk. Up to 5,900 psi in tensile strength. Often used in applications requiring excellent flex life. Parts fabricated from this resin have excellent physical and electrical properties.( 精细分割“蓬松“20微米的颗粒。 250 g / L的大部分。高达5,900 psi的拉伸强度。常用于要求具有出色的弹性生活中的应用。这种树脂制成的零件具有优异的物理和电气性能)
8A: Pelletized 510-micron particles. 690-g/L bulk density. Up to 4,480 psi in tensile strength. Resin particles are preformed using lower preform pressures. Parts fabricated from this resin have superior physical and electrical properties.( 球团510微米的颗粒。 690 g / L的体积密度。高达4,480 psi的拉伸强度。树脂颗粒预制件预制使用较低的压力。这种树脂制成的零件具有优良的物理和电气性能)
807-N: A multi-purpose PTFE resin which yields high productivity due to its high fill density. It has an excellent combination of handleability, processability, machinability and end-use properties.Note: Teflon® 807-N meets the requirements of ASTM D 4894-91a, type IV, grade 2 (except for tensile properties).( 多用途聚四氟乙烯树脂产量高生产力，由于其高填充密度。它有一个可操作性，加工性能，可加工性和最终使用性能的完美结合。注：特富龙®807- N的符合美国ASTMð4894-91a，IV型的要求，2级（除拉伸性能）。)
NXT70: A fine-cut resin designed for compression molding of blocks and sheets and for use as a base resin for compounds.( 阿细切树脂设计 缩成型块和片并作为基础树脂的化合物的使用)
NXT75: A fine-cut resin designed for eneral compression molding of blocks and sheets and for use as a base resin for compounds.( 阿细切树脂设计 和片并作为基础树脂使用的化合物一般压缩成型)
NXT85: Chemically modified free-flow granular molding resin can be converted to parts by isostatic, billet, and sheet molding methods, as well as ram extrusion.( 化学改性的自由流动颗粒成型树脂可转换为以均衡，部分钢坯和薄板成型方法，以及RAM的挤压)